Kette AH – ASH Tabelle
Bezeichnung | Ø Nenndicke d | Zulässige Toleranz | Teilung p | b 2 max. | b 1 min. | Masse kg/m ≅ | Standard Stranglänge | Prüfkraft kN | Mindestbruchkraft kN* |
|||
mm | Gliederanzahl | Länge mm | kN B | kN C/ CS | B | C / CS | ||||||
AH 22 | 22 | +0.7 -0.2 | 86 ± 0.9 | 75 | 26 | 95 | 291 | 25026 | 183 | 160 | 305 | 270 |
ASH 26 | 26 | +0.8 -0.2 | 92 ± 1.0 | 87 | 31 | 136 | 273 | 25116 | 255 | 223 | 425 | 370 |
AH 26 | 26 | +0.8 -0.2 | 100 ±1.0 | 87 | 31 | 133 | 281 | 28100 | 255 | 223 | 425 | 370 |
ASH 30 | 30 | +1.0 -0.2 | 108 ± 1.2 | 101 | 36 | 180 | 191 | 20628 | 340 | 300 | 565 | 500 |
AH 30 | 30 | +1.0 -0.2 | 120 ±1.2 | 101 | 36 | 175 | 209 | 25080 | 340 | 300 | 565 | 500 |
ASH 34 | 34 | +1.2 -0.4 | 126 ± 1.2 | 113 | 39 | 238 | 197 | 24822 | 425 | 370 | 710 | 621 |
AH 34 | 34 | +1.2 -0.4 | 136 ± 1.2 | 113 | 39 | 238 | 107 | 26792 | 425 | 370 | 710 | 621 |
AH 38 | 38 | +1.2 -0.4 | 144 ± 1.2 | 127 | 44 | 300 | 143 | 20592 | 530 | 480 | 910 | 800 |
(*) Tolleranza -10% secondo i lotti di produzione. Tolerance -10%, depending on batches. Toleranz -10% nach Charge.
Qualità / Quality / Qualität | AH / ASH | B | C | CS |
---|---|---|---|---|
Durezza superficiale Surface hardness Oberflächenhärte | HV30 min. (1) | 820 | 820 | 830 |
Profondità totale di cementazione Total carburizing depth Gesamthärtetiefe | HTÄ ×d min. (1) | 0.11 (3) | 0.14 (4) | 0.15 (7) |
Profondità efficace di cementazione Effective case hardening depth Tatsächliche Härtetiefe | CHD 550 HV1 EN ISO 2639 ×d min. (1,2) | 0.07 (5) | 0.09 (6) | 0.10 (8) |
Carico unitario di rottura Breaking stress Mindestbruchlast | N/mm 2 | 400 | 350 | 350 |
Carico unitario di prova Proof stress Prüflast | N/mm 2 | 240 | 210 | 210 |
Materiale / Material / Material | CrNi / NiCrMo alloy | CrNi / NiCrMo alloy | CrNi / NiCrMo alloy | CrNi / NiCrMo alloy |
Allungamento a rottura: 2%; Breaking elongation: 2% ; Bruchdehnung: 2%